Main: DawnsYarn

Dawn's Yarn Assignment: Conductive Spinning

Due March 10, 2010

I made yarn! Well, actually, I made 3 yarns, but I will only discuss my final yarn in detail. My final yarn is a two-ply wool-steel blend. One of the plies is wool-only and the other is a mixture of conductive steel fibers and wool. The plies were spun using a drop-spindle and then plied by hand. The yarn was not soaked in hot water, so the twist isn't set and its not quite a "finished" yarn. However, I am happy with it! My goal was to learn to spin, and by spinning both a normal wool ply and a wool-steel blend, I was able to experiment with the difference between spinning natural and man-made fibers. Also, I was hoping to make a conductive yarn but I wasn't sure how much steel I needed to spin into the yarn for that. Luckily the amount of steel I added to the second ply was enough to have good conductance over the whole 2 meter yarn.

Close-up pictures of the yarn show the conductive steel fibers running through the second ply. The steel fibers didn't integrate very well with the wool even though I was trying to combine them evenly while spinning.


Yarn Specifications

The following properties of the yarn were measured:


Extra Credit Measurements: Tex

I also measured the tex of the yarn. First I weighed the yarn I made. Then I converted its weight into a weight (in grams) per length (meters), which was 2.365 grams/meter. Since tex is the weight of 1000 meters of yarn, I multiplied 2.365 by 1000 to find that the tex of my yarn is 2,365.


Thoughts, Improvements, Suggestions